Raman studies of Pd-C nanocomposites

Czasopismo: Central European Journal of Physics   Tom: 11, Zeszyt: 2, Strony: 245-250
ISSN:  1895-1082
Wydawca:  VERSITA, SOLIPSKA 14A-1, 02-482 WARSAW, POLAND
Opublikowano: Luty 2013
 
  Autorzy / Redaktorzy / Twórcy
Imię i nazwisko Wydział Katedra Procent
udziału		 Liczba
punktów
Radosław Belka orcid logoWEAiIKatedra Systemów Informatycznych *256.67  
Małgorzata Suchańska orcid logoWEAiIKatedra Systemów Informatycznych *256.67  
Elżbieta Czerwosz25.00  
Justyna Kęczkowska orcid logoWEAiIKatedra Systemów Informatycznych *256.67  

Grupa MNiSW:  Publikacja w czasopismach wymienionych w wykazie ministra MNiSzW (część A)
Punkty MNiSW: 20
Klasyfikacja Web of Science: Article

Pełny tekstPełny tekst     DOI LogoDOI     Web of Science Logo Web of Science     Web of Science LogoYADDA/CEON    
Keywords:

Pd-C nanostructures  fullerene  Raman spectroscopy  PVD/CVD 


Abstract:

The results of studying palladium-carbon (Pd-C) nanocomposites using Raman spectroscopy are presented. This method has been used for studying samples having various palladium content, prepared by a one-step Physical Vapour Deposition (PVD) process and a Chemical Vapour Deposition (two-step PVD/CVD) process using different process parameters. For samples obtained by PVD, the vibration bands characteristic of C60 fullerene molecules were observed in the spectra, whereas for layers obtained by PVD/CVD, the Raman spectra displayed mainly D and G bands characteristic solely of the prescence of graphite-like layers’ vibrations. The analysis of the obtained Raman spectra reveals that its shape is affected by many parameters including type of substrate, temperature, and the percentage content of Pd in the studied layer. The quantitative analysis of spectra for layers obtained using the PVD/CVD process shows a difference in the relative intensity of bands D and G, reflecting the different degrees of amorphisation in the investigated nanocomposites.